Bostik Elastic Bonding Adhesives for Marine
Bostik Elastic Adhesives for Marine
Marine Bonding Applications
To ensure the seaworthiness of any vessel, Bostik offers a variety of elastic bonding adhesive systems that provide exceptional weather and water-resistant properties. The range of marine products has been engineered for high performance elastic bonding of marine substrates; plywood, aluminum, fiberglass or other composite materials used in building marine vessels. These products can be used for permanent bonding or for service and repair.
To ensure the seaworthiness of any vessel, Bostik offers a variety of elastic bonding adhesive systems that provide exceptional weather and water-resistant properties. The range of marine products has been engineered for high performance elastic bonding of marine substrates; plywood, aluminum, fiberglass or other composite materials used in building marine vessels. These products can be used for permanent bonding or for service and repair.
Item # |
Polymer Base |
Curing Method |
Skin Forming Time |
Complete Cure (0.125" Head) |
Tensile Strength |
---|---|---|---|---|---|
920 | Polymer Base N/A Urethane | Curing Method N/A Moisture | Skin Forming Time N/A 90 min | Complete Cure (0.125" Head) N/A 3-6 days | Tensile Strength N/A 175 psi |
920FS | Polymer Base N/A Urethane | Curing Method N/A Moisture | Skin Forming Time N/A 30-40 min | Complete Cure (0.125" Head) N/A 1.5-3 days | Tensile Strength N/A 175 psi |
940A | Polymer Base N/A SMP | Curing Method N/A Moisture | Skin Forming Time N/A 90 min | Complete Cure (0.125" Head) N/A 1-2 days | Tensile Strength N/A 300 psi |
940FSA | Polymer Base N/A SMP | Curing Method N/A Moisture | Skin Forming Time N/A 45 min | Complete Cure (0.125" Head) N/A 24 hours | Tensile Strength N/A 450 psi |
960SR | Polymer Base N/A SPS | Curing Method N/A Moisture | Skin Forming Time N/A 10-15 min | Complete Cure (0.125" Head) N/A 24 hours | Tensile Strength N/A 150 psi |
965FS | Polymer Base N/A SPS | Curing Method N/A Moisture | Skin Forming Time N/A 30 min | Complete Cure (0.125" Head) N/A 24 hours | Tensile Strength N/A 255 psi |
70-08A | Polymer Base N/A SMP | Curing Method N/A Moisture | Skin Forming Time N/A 10-15 min | Complete Cure (0.125" Head) N/A 24 hours | Tensile Strength N/A 425 psi |
70-11 | Polymer Base N/A SMP | Curing Method N/A Moisture | Skin Forming Time N/A 30-45 min | Complete Cure (0.125" Head) N/A 24-36 hours | Tensile Strength N/A 335 psi |
70-12 | Polymer Base N/A SMP | Curing Method N/A Moisture | Skin Forming Time N/A 10-15 min | Complete Cure (0.125" Head) N/A 24 hours | Tensile Strength N/A 580 psi |