Bostik Elastic Sealing Adhesives for Marine
Bostik Elastic Adhesives for Marine
Marine Sealing Applications
Bostik marine sealants form a very durable, elastomeric waterproof seal for applications above and below the waterline. Some of these products offer excellent UV resistance and will not shrink, chalk, or crack over time. In most cases, surface pretreatment is not required. This translates to a reduction in production time, costs, and environmental/VOC concerns. Bostik marine sealants are easy to use, easy to sand and paint, non-gassing products that stand up to the harshest marine environments. Used for permanent sealing or for service and repair, their applications include sealing deck hardware and hatches, around doors and portholes, deck-to- hull assembly, thru-hull fittings and seams, keel joints and undermoldings, or bedding navigational equipment.
Bostik marine sealants form a very durable, elastomeric waterproof seal for applications above and below the waterline. Some of these products offer excellent UV resistance and will not shrink, chalk, or crack over time. In most cases, surface pretreatment is not required. This translates to a reduction in production time, costs, and environmental/VOC concerns. Bostik marine sealants are easy to use, easy to sand and paint, non-gassing products that stand up to the harshest marine environments. Used for permanent sealing or for service and repair, their applications include sealing deck hardware and hatches, around doors and portholes, deck-to- hull assembly, thru-hull fittings and seams, keel joints and undermoldings, or bedding navigational equipment.
Item # |
Polymer Base |
Curing Method |
Skin Forming Time |
Complete Cure (0.125" Head) |
Tensile Strength |
---|---|---|---|---|---|
920 | Polymer Base N/A Urethane | Curing Method N/A Moisture | Skin Forming Time N/A 90 min | Complete Cure (0.125" Head) N/A 3-6 days | Tensile Strength N/A 175 psi |
920FS | Polymer Base N/A Urethane | Curing Method N/A Moisture | Skin Forming Time N/A 30-40 min | Complete Cure (0.125" Head) N/A 1.5-3 days | Tensile Strength N/A 175 psi |
940A | Polymer Base N/A SMP | Curing Method N/A Moisture | Skin Forming Time N/A 90 min | Complete Cure (0.125" Head) N/A 1-2 days | Tensile Strength N/A 300 psi |
940FSA | Polymer Base N/A SMP | Curing Method N/A Moisture | Skin Forming Time N/A 45 min | Complete Cure (0.125" Head) N/A 24 hours | Tensile Strength N/A 450 psi |
960SR | Polymer Base N/A SPS | Curing Method N/A Moisture | Skin Forming Time N/A 10-15 min | Complete Cure (0.125" Head) N/A 24 hours | Tensile Strength N/A 150 psi |
965FS | Polymer Base N/A SPS | Curing Method N/A Moisture | Skin Forming Time N/A 30 min | Complete Cure (0.125" Head) N/A 24 hours | Tensile Strength N/A 255 psi |
70-08A | Polymer Base N/A SMP | Curing Method N/A Moisture | Skin Forming Time N/A 10-15 min | Complete Cure (0.125" Head) N/A 24 hours | Tensile Strength N/A 425 psi |
70-11 | Polymer Base N/A SMP | Curing Method N/A Moisture | Skin Forming Time N/A 30-45 min | Complete Cure (0.125" Head) N/A 24-36 hours | Tensile Strength N/A 335 psi |
70-12 | Polymer Base N/A SMP | Curing Method N/A Moisture | Skin Forming Time N/A 10-15 min | Complete Cure (0.125" Head) N/A 24 hours | Tensile Strength N/A 580 psi |