Item # |
Polymer Base |
Curing Method |
Skin Forming Time |
Complete Cure (0.125" Head) |
Tensile Strength |
|---|---|---|---|---|---|
| 1100FS 1100FS/Asset/a1233.jpg | Polymer Base N/A Urethane | Curing Method N/A Moisture | Skin Forming Time N/A 60 min | Complete Cure (0.125" Head) N/A 1.5-3 days | Tensile Strength N/A 150 psi |
| 70-03A 70-03A/Asset/a1233.jpg | Polymer Base N/A SMP | Curing Method N/A Moisture | Skin Forming Time N/A 10-15 min | Complete Cure (0.125" Head) N/A 24 hours | Tensile Strength N/A 400 psi |
| 70-03A SK 70-03A SK/Asset/a1233.jpg | Polymer Base N/A SMP | Curing Method N/A Moisture | Skin Forming Time N/A 10-15 min | Complete Cure (0.125" Head) N/A 24-36 hours | Tensile Strength N/A 400 psi |
| 70-05A 70-05A/Asset/a1233.jpg | Polymer Base N/A SMP | Curing Method N/A Moisture | Skin Forming Time N/A 15 min | Complete Cure (0.125" Head) N/A 24 hours | Tensile Strength N/A 500 psi |
| 70-07A 70-07A/Asset/a1233.jpg | Polymer Base N/A SMP | Curing Method N/A Moisture | Skin Forming Time N/A 30 min | Complete Cure (0.125" Head) N/A 24-36 hours | Tensile Strength N/A 225 psi |
| 70-08A 70-08A/Asset/a1233.jpg | Polymer Base N/A SMP | Curing Method N/A Moisture | Skin Forming Time N/A 10-15 min | Complete Cure (0.125" Head) N/A 24 hours | Tensile Strength N/A 425 psi |
| 70-09 70-09/Asset/a1233.jpg | Polymer Base N/A SMP | Curing Method N/A Moisture | Skin Forming Time N/A 10-15 min | Complete Cure (0.125" Head) N/A 24 hours | Tensile Strength N/A 425 psi |
| 70-11 70-11/Asset/a1233.jpg | Polymer Base N/A SMP | Curing Method N/A Moisture | Skin Forming Time N/A 30-45 min | Complete Cure (0.125" Head) N/A 24-36 hours | Tensile Strength N/A 335 psi |
| 70-12 70-12/Asset/a1233.jpg | Polymer Base N/A SMP | Curing Method N/A Moisture | Skin Forming Time N/A 10-15 min | Complete Cure (0.125" Head) N/A 24 hours | Tensile Strength N/A 580 psi |
| LoVOC LoVOC/Asset/a1233.jpg | Polymer Base N/A Urethane | Curing Method N/A Moisture | Skin Forming Time N/A 45 min | Complete Cure (0.125" Head) N/A 24 hours | Tensile Strength N/A 125 psi |
| Liquid Rivet 1152 FS Liquid Rivet 1152 FS/Asset/a1233.jpg | Polymer Base N/A Urethane | Curing Method N/A Moisture | Skin Forming Time N/A 30-45 min | Complete Cure (0.125" Head) N/A 24 hours | Tensile Strength N/A 250 psi |
| 2100 SPS 2100 SPS/Asset/a1233.jpg | Polymer Base N/A SPS | Curing Method N/A Moisture | Skin Forming Time N/A 50 min | Complete Cure (0.125" Head) N/A 24 hours | Tensile Strength N/A 175 psi |
| 2200 TS 2200 TS/Asset/a1233.jpg | Polymer Base N/A SPS | Curing Method N/A Moisture | Skin Forming Time N/A 30-40 min | Complete Cure (0.125" Head) N/A 24 hours | Tensile Strength N/A 250 psi |
| B-Component B-Component/Asset/a1233.jpg | Polymer Base N/A Proprietary | Curing Method N/A | Skin Forming Time N/A | Complete Cure (0.125" Head) N/A | Tensile Strength N/A |
| Prep M Prep M/Asset/a1233.jpg | Polymer Base N/A Solvent-based | Curing Method N/A | Skin Forming Time N/A | Complete Cure (0.125" Head) N/A | Tensile Strength N/A |
| Prep G Prep G/Asset/a1233.jpg | Polymer Base N/A Solvent-based | Curing Method N/A | Skin Forming Time N/A | Complete Cure (0.125" Head) N/A <30 mins | Tensile Strength N/A |